Fiberon™ PA6-GF25 – High-Performance Glass Fiber Reinforced Nylon
Fiberon™ PA6-GF25 (formerly PolyMide™ PA6-GF) is a Nylon 6 filament reinforced with 25% glass fiber for 1.75mm FDM printers. The material offers excellent thermal and mechanical properties without sacrificing interlayer adhesion, resulting in rigid, heat-resistant, and dimensionally stable parts. Thanks to its high thermal resistance and the robustness typical of nylon-glass composites, it is suitable for technical and industrial components subjected to mechanical stress and high operating temperatures.
Key Features
- 25% Glass Fiber Reinforcement: high stiffness and mechanical strength compared to pure Nylon
- Excellent Heat Resistance: HDT up to 191°C (0.45 MPa)
- Good Interlayer Adhesion: despite the glass fiber loading, it maintains reliable printability
- Hygroscopic: requires drying and storage in a dry environment (relative humidity below 20%)
- Post-print Annealing Recommended: 100°C for 16 hours to maximize mechanical performance
Technical Specifications
| Parameter | Value |
|---|---|
| Diameter | 1.75 mm |
| Density | 1.20 g/cm³ |
| Tensile Strength (X-Y, dry) | 80.1 ± 1.8 MPa |
| Elongation at Break (X-Y, dry) | 2.4 ± 0.2% |
| Flexural Modulus (X-Y, dry) | 4314.2 ± 120.6 MPa |
| Flexural Strength (X-Y, dry) | 133.8 ± 4.7 MPa |
| Charpy Impact Strength with Notch (X-Y, dry) | 10.0 ± 0.7 kJ/m² |
| HDT (0.45 MPa) | 191 °C |
| HDT (1.8 MPa) | 157 °C |
| Glass Transition Temperature | 70.4 °C |
Printing Settings
| Parameter | Value |
|---|---|
| Nozzle Temp. | 280–300 °C |
| Bed Temp. | 40–50 °C |
| Speed | up to 300 mm/s |
| Cooling fan | Off |
| Nozzle | Hardened or ruby nozzle recommended (rapid wear of brass nozzle) |
| Drying | 100 °C for 10 hours |
| Annealing | 100 °C for 16 hours |
| Recommended Support | PolyDissolve™ S1 |
Printer Compatibility
Requires a 1.75mm FDM printer with a hotend capable of reaching at least 300°C, equipped with a wear-resistant nozzle (hardened steel or ruby). It does not require a heated chamber but benefits from a controlled environment for dimensional stability.
Applications
- Mechanical components subjected to load and heat
- Brackets, supports, and industrial structural parts
- Tools and jigs for use in harsh environments
- Replacement for injection-molded filled nylon parts
Domande frequenti
Che caratteristiche ha il Fiberon™ PA6-GF25?
Il rinforzo in fibra di vetro al 25% lo rende estremamente rigido e facile da processare, un'ottima base per parti strutturali che non richiedono le prestazioni della fibra di carbonio.
Per cosa è indicato il PA6-GF25?
È indicato per parti strutturali e componenti tecnici che richiedono elevata rigidità dimensionale, con un buon equilibrio tra costo e prestazioni.
Materia Polymers spedisce in tutta Italia?
Sì, spediamo in tutta Italia con spedizione standard gratuita a partire da €49,90 di spesa.