Fiberon™ PA6-CF20 – High Rigidity Carbon Fiber Reinforced Nylon 6
Fiberon™ PA6-CF20 is a Nylon 6 filament reinforced with 20% carbon fiber for 1.75mm FDM printers. The carbon fiber reinforcement significantly improves rigidity, mechanical strength, and heat resistance while maintaining excellent layer adhesion. Thanks to these properties, it is one of the highest-performing Fiberon materials in the range, suitable for replacing metal or injection-molded filled nylon components in demanding technical applications.
Key Features
- 20% carbon fiber reinforcement: very high rigidity and mechanical strength
- Excellent heat resistance: HDT up to 215°C (0.45 MPa)
- Excellent layer adhesion: despite the high fiber load
- Hygroscopic: requires drying and storage in a dry environment (relative humidity below 20%)
- Recommended post-print annealing: 100°C for 16 hours to maximize mechanical performance
Technical Specifications
| Parameter | Value |
|---|---|
| Diameter | 1.75 mm |
| Density | 1.17 g/cm³ |
| Tensile Strength (X-Y, dry) | 109.3 ± 2.4 MPa |
| Elongation at Break (X-Y, dry) | 2.1 ± 0.2% |
| Flexural Modulus (X-Y, dry) | 7037.6 ± 205.4 MPa |
| Flexural Strength (X-Y, dry) | 161.0 ± 3.9 MPa |
| Charpy Notched Impact (X-Y, dry) | 11.0 ± 0.3 kJ/m² |
| HDT (0.45 MPa) | 215 °C |
| HDT (1.8 MPa) | 173 °C |
| Melting Temperature | 218.5 °C |
Print Settings
| Parameter | Value |
|---|---|
| Nozzle Temp. | 280–300 °C |
| Bed Temp. | 40–50 °C |
| Speed | up to 300 mm/s |
| Cooling fan | Off |
| Nozzle | Hardened steel or ruby nozzle recommended (rapid wear of brass nozzle) |
| Drying | 100 °C for 10 hours |
| Annealing | 100 °C for 16 hours |
| Recommended support | PolyDissolve™ S1 |
Printer Compatibility
Requires a 1.75mm FDM printer with a hotend capable of reaching at least 300°C, equipped with a wear-resistant nozzle (hardened steel or ruby). The high carbon fiber load makes the material quite abrasive to the extruder.
Applications
- Structural components subject to high loads
- Replacement for metal or injection-molded filled nylon parts
- Brackets, gears, and high-performance technical components
- Heat-resistant industrial equipment
Domande frequenti
Che caratteristiche ha il Fiberon™ PA6-CF20?
Il rinforzo al 20% in fibra di carbonio offre resistenza e tenacità elevate insieme a un'ottima resistenza al calore, per applicazioni industriali impegnative.
Materia Polymers spedisce in tutta Italia?
Sì, spediamo in tutta Italia con spedizione standard gratuita a partire da €49,90 di spesa.