Fiberon™ PA12-CF10 – Low-Hygroscopicity Carbon Fiber Reinforced Nylon 12
Fiberon™ PA12-CF10 is a long-chain co-polyamide (PA12) filament reinforced with 10% carbon fiber for 1.75mm FDM printers. Thanks to its chemical structure, it has much lower moisture sensitivity compared to PA6/66-based materials, while maintaining superior mechanical properties compared to common PA12. The carbon fiber reinforcement, combined with Warp-free™ technology, further improves the dimensional stability of printed parts, reducing warping and shrinkage.
Key Features
- Low hygroscopicity: absorbs much less moisture than PA6/66 nylons, simplifying storage and printing
- 10% carbon fiber reinforcement: greater stiffness and strength compared to unreinforced PA12
- Warp-free™ technology: minimizes warping and improves dimensional stability
- Post-printing annealing recommended: 100°C for 16 hours to maximize mechanical performance
Technical Specifications
| Parameter | Value |
|---|---|
| Diameter | 1.75 mm |
| Density | 1.06 g/cm³ |
| Tensile Strength (X-Y, dry) | 77.4 ± 1.1 MPa |
| Elongation at Break (X-Y, dry) | 4.2 ± 0.4% |
| Flexural Modulus (X-Y, dry) | 2886.5 ± 144.8 MPa |
| Flexural Strength (X-Y, dry) | 112.4 ± 1.0 MPa |
| Notched Charpy Impact (X-Y, dry) | 9.9 ± 0.7 kJ/m² |
| HDT (0.45 MPa) | 131 °C |
| HDT (1.8 MPa) | 105 °C |
| Melting Temperature | 171 °C |
Printing Settings
| Parameter | Value |
|---|---|
| Nozzle Temp. | 280–300 °C |
| Bed Temp. | 40–50 °C |
| Speed | up to 300 mm/s |
| Cooling fan | Off |
| Nozzle | Hardened steel or ruby nozzle recommended (rapid wear of brass nozzle) |
| Drying | 100 °C for 10 hours |
| Annealing | 100 °C for 16 hours |
| Recommended support | PolyDissolve™ S1 or PolySupport™ for PA12 |
Printer Compatibility
Requires a 1.75mm FDM printer with a hotend capable of reaching at least 300°C, equipped with a wear-resistant nozzle (hardened steel or ruby). Recommended for printers with a direct extruder or robust Bowden setup for handling reinforced material.
Applications
- Mechanical components requiring dimensional stability in humid environments
- Rigid and lightweight functional parts
- Technical brackets and supports for industrial use
- High-performance functional prototyping
Domande frequenti
Che caratteristiche ha il Fiberon™ PA12-CF10?
Il rinforzo al 10% in fibra di carbonio aggiunge rigidità mantenendo la bassa sensibilità all'umidità tipica del PA12, oltre a una buona facilità di stampa.